Orthodontic resins loaded with niobium silicate particles: Impact of filler concentration on the physicochemical and biological properties.

OBJECTIVES: White spot lesions (WSL) are prevalent in patients using orthodontic appliances. The presence of ion-releasing compounds in the tooth-appliance interface may limit enamel demineralization to control WSL incidence. Thus, this study aims to evaluate the mineral formation on SiNb-containing experimental orthodontic resins and the influence of these fillers on the physicochemical and biological properties of developed materials. MATERIALS AND METHODS: The SiNb particles were synthesized via the sol-gel route and characterized by their molecular structure and morphology. Photopolymerizable orthodontic resins were produced with a 75 wt% Bis-GMA/25 wt% TEGDMA and 10 wt%, 20 wt%, or 30 wt% addition of SiNb. A control group was formulated without SiNb. These resins were tested for their degree of conversion, softening in solvent, cytotoxicity in fibroblasts, flexural strength, shear bond strength (SBS), and mineral deposition. RESULTS: The addition of 10 wt% of SiNb did not impair the conversion of monomers, cytotoxicity, and flexural strength. All groups with SiNb addition presented similar softening in solvent. The presence of these particles did not affect the bond strength between metallic brackets and enamel, with SBS values ranging from 16.41 to 18.66 MPa. The mineral deposition was observed for all groups. CONCLUSION: The use of niobium silicate as filler particles in resins may be a strategy for the adhesion of orthodontic appliances. The 10 wt% SiNb concentration resulted in a material with suitable physicochemical and biological properties while maintaining the bond strength to tooth enamel and promoting mineral deposition.

Effect of light attenuation through veneers on bond strength of adhesives with photoinitiator combinations.

This study aimed to evaluate the effect of light attenuation through ceramic veneers and resin cement on degree of conversion (DC), cohesive strength (CS), and microshear bond strength (µSBS) of experimental adhesive systems. Experimental etch-and-rinse and self-etch adhesives were combined with different ratios of camphorquinone (CQ) and diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) photoinitiators: CQ-only; 3CQ:1TPO; 1CQ:1TPO; 1CQ:3TPO and TPO-only. Square-shaped ceramic veneer (IPS Empress Esthetic, Ivoclar Vivadent) (n = 10; 10mm long x 10mm wide x 0.5mm thick) and resin cement specimens (Variolink Esthetic LC, Ivoclar Vivadent) (n = 10; 10 mm long x 10 mm wide and 0.3 mm thick) were prepared. Light transmittance of a multiple-peak LED (Bluephase G2, Ivoclar Vivadent) was measured through restorative materials using a spectrometer (n = 5). Adhesive specimens were analyzed for DC, CS, and µSBS by light-curing the adhesive with or without (control) ceramic veneer, and with resin cement fixed to output region of the light-curing tip (n = 10). Data were submitted to ANOVA and Tukey's test (α = 0.05). Total light transmittance through the restorative materials was attenuated, and this attenuation was more evident for the violet spectrum. The DC for the TPO groups in ratios up to 1CQ:1TPO was similar to the control. 1CQ:3TPO showed lower values for CS. µSBS was reduced for all groups with light attenuation, but lower values were observed for 1CQ:3TPO and TPO-only. In conclusion, light transmission was reduced with interposed restorative materials. Adhesives combined with CQ and TPO up to 1CQ:1TPO showed greater cure efficiency and mechanical properties compared with a higher amount of TPO.

Effect of light attenuation through veneers on bond strength of adhesives with photoinitiator combinations

Abstract This study aimed to evaluate the effect of light attenuation through ceramic veneers and resin cement on degree of conversion (DC), cohesive strength (CS), and microshear bond strength (μSBS) of experimental adhesive systems. Experimental etch-and-rinse and self-etch adhesives were combined with different ratios of camphorquinone (CQ) and diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) photoinitiators: CQ-only; 3CQ:1TPO; 1CQ:1TPO; 1CQ:3TPO and TPO-only. Square-shaped ceramic veneer (IPS Empress Esthetic, Ivoclar Vivadent) (n = 10; 10mm long x 10mm wide x 0.5mm thick) and resin cement specimens (Variolink Esthetic LC, Ivoclar Vivadent) (n = 10; 10 mm long x 10 mm wide and 0.3 mm thick) were prepared. Light transmittance of a multiple-peak LED (Bluephase G2, Ivoclar Vivadent) was measured through restorative materials using a spectrometer (n = 5). Adhesive specimens were analyzed for DC, CS, and μSBS by light-curing the adhesive with or without (control) ceramic veneer, and with resin cement fixed to output region of the light-curing tip (n = 10). Data were submitted to ANOVA and Tukey's test (α = 0.05). Total light transmittance through the restorative materials was attenuated, and this attenuation was more evident for the violet spectrum. The DC for the TPO groups in ratios up to 1CQ:1TPO was similar to the control. 1CQ:3TPO showed lower values for CS. μSBS was reduced for all groups with light attenuation, but lower values were observed for 1CQ:3TPO and TPO-only. In conclusion, light transmission was reduced with interposed restorative materials. Adhesives combined with CQ and TPO up to 1CQ:1TPO showed greater cure efficiency and mechanical properties compared with a higher amount of TPO.

Incorporation of amoxicillin-loaded microspheres in mineral trioxide aggregate cement: an in vitro study.

OBJECTIVES: In this study, we investigated the potential of amoxicillin-loaded polymeric microspheres to be delivered to tooth root infection sites via a bioactive reparative cement. MATERIALS AND METHODS: Amoxicillin-loaded microspheres were synthesized by a spray-dray method and incorporated at 2.5% and 5% into a mineral trioxide aggregate cement clinically used to induce a mineralized barrier at the root tip of young permanent teeth with incomplete root development and necrotic pulp. The formulations were modified in liquid:powder ratios and in composition by the microspheres. The optimized formulations were evaluated in vitro for physical and mechanical eligibility. The morphology of microspheres was observed under scanning electron microscopy. RESULTS: The optimized cement formulation containing microspheres at 5% exhibited a delayed-release response and maintained its fundamental functional properties. When mixed with amoxicillin-loaded microspheres, the setting times of both test materials significantly increased. The diametral tensile strength of cement containing microspheres at 5% was similar to control. However, phytic acid had no effect on this outcome (p > 0.05). When mixed with modified liquid:powder ratio, the setting time was significantly longer than that original liquid:powder ratio (p < 0.05). CONCLUSIONS: Lack of optimal concentrations of antibiotics at anatomical sites of the dental tissues is a hallmark of recurrent endodontic infections. Therefore, targeting the controlled release of broad-spectrum antibiotics may improve the therapeutic outcomes of current treatments. Overall, these results indicate that the carry of amoxicillin by microspheres could provide an alternative strategy for the local delivery of antibiotics for the management of tooth infections.

Niobium silicate particles as bioactive fillers for composite resins.

OBJECTIVES: This study aimed to evaluate the influence of niobium silicate (SiNb) particles in the physicomechanical and biological properties of an experimental composite resin. METHODS: The SiNb particles were incorporated (50 wt%) into a polymeric matrix formulated with 70 wt% Bisphenol A-Glycidyl Methacrylate and 30 wt% Triethylene Glycol Dimethacrylate to formulate an experimental composite resin. A control group was formulated with barium silicate glass (SiBa) as filler for the same polymeric matrix. The composite resins were tested for their refractive index, polymerization kinetics, flexural strength, radiopacity, softening in solvent, pH, cytotoxicity and mineral deposition. RESULTS: The SiBa group presented refractive index results between 1.50 and 1.52 and the SiNb between 1.43-1.45. No statistically significant difference in the degree of conversion, flexural strength, and softening in solvent was observed between different groups. Radiopacity was lower for SiNb, while the addition of these particles increased cell viability. The pH was increased for all groups after immersion. The mineral deposition analysis resulted in increased deposition above specimens after the immersion in SBF. SIGNIFICANCE: Niobium silicate particles may be used as an alternative inorganic filler to achieve an adequate balance between physical-chemical and biological properties for the development of bioactive composite resins.

Addition of phosphates and chlorhexidine to resin-modified MTA materials.

To evaluate the properties of experimental mineral trioxide aggregate (MTA) resin-modified materials for root-end filling procedures, varying their compositions regarding the addition of hydroxiapatite (HA) or dicalcium phosphate dihydrate, with or without chlorhexidine digluconate. White MTA (Angelus, Londrina, Brazil) was used as a reference material. Degree of conversion (DC) was evaluated by Fourier transformed infrared (FTIr) spectroscopy (n = 5). Flowability (n = 3) and radiopacity (n = 3) were evaluated following ISO 6876:2001 methods. For splitting tensile strength analysis, cylindrical samples (n = 10) were subjected to compressive load using a universal testing machine (Instron Corporation, Norwood, MA). Water sorption and solubility tests were performed according to ISO 4049:2009 methods. Calcium ion release and pH analysis (n = 10) were evaluated using a pH meter (Orion, Watsonville, CA). Cytotoxicity (n = 8) of materials extracts was evaluated as cell viability percentage. Statistical analysis was performed using Kolmogorov-Smirnov for normal distribution and data was subjected to one-way ANOVA and Tukey test (α = 0.05). Addition of chlorhexidine digluconate reduced DC mean values for experimental materials (<50%). White MTA demonstrated lower flowability (5.3 mm) and higher radiopacity (9.8 mm Al), splitting tensile strength (9.1 MPa), solubility (8.2 µg/mm3 ), calcium ion release (~26.5 ppm), cytotoxicity (55.2%), and pH mean values (10.8), when compared to experimental materials. All groups demonstrated a decrease in calcium release (<85%) and pH (<13%). Formulation containing HA demonstrated similar pH values after 28 days when compared to white MTA. Evaluated experimental resin-modified MTA based materials without chlorhexidine digluconate showed satisfactory results for all physico-chemical properties tested and cytotoxicity. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 2195-2201, 2019.

Iodonium salt incorporation in dental adhesives and its relation with degree of conversion, ultimate tensile strength, cell viability, and oxidative stress.

OBJECTIVE: The aim of this study was to evaluate the degree of conversion, ultimate tensile strength, cell viability, and oxidative stress of two different ternary initiation systems, using two photoinitiation polymerization times. METHODS: The groups investigated were camphorquinone (CQ); CQ and diphenyleneiodonium hexafluorophosphate (DPI); CQ and ethyl 4-dimethylamine benzoate (EDAB); and CQ, EDAB, and DPI, with EDAB in high and low concentration. To assess the degree of conversion (DC) and the ultimate tensile strength (UTS), a real-time Fourier transform infrared spectroscopy and a universal test machine Emic DL-500 were used, respectively. Cell viability and oxidative stress were evaluated by MTT (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide), superoxide dismutase (SOD), total sulfhydryl (SH) content, and thiobarbituric acid reactive species (TBARS) formation assays. RESULTS: Slight lower cell viability was shown when DPI was associated with high concentrations of EDAB; this reduction seemed to be attenuated when lower concentrations of EDAB were used. When EDAB and DPI were associated, no oxidative damage was shown. The degree of conversion was increased in the ternary systems (CQ + EDAB lower concentration + DPI) group, which did not affect the UTS, cytotoxicity, and oxidative stress parameters. The polymerization time did not affect cell viability, total SH, and TBARS; however, a slight increase was shown in SOD levels. CLINICAL RELEVANCE: Our study emphasizes the relevance of incorporating the third element-iodonium salt-in a binary adhesive systems composed exclusively of CQ and EDAB.

Development and characterization of a novel bulk-fill elastomeric temporary restorative composite

Abstract Objectives: This study investigated the physical and mechanical properties, antibacterial effect and biocompatibility of novel elastomeric temporary resin-based filling materials (TFMs) containing zinc methacrylate (ZM). Material and Methods: Experimental TFMs were prepared by mixing the zinc methacrylate with monomer, co-monomer, photoinitiator and fillers. A ZM concentration of 0 (control), 0.5% (Z0.5); 1% (Z1), 2% (Z2), or 5% (ZM5) wt% was added to the TFMs. Fermit-N (F) was used for comparison with the experimental material. Microleakage, water sorption/solubility, degree of conversion, depth of cure, ultimate tensile strength, and hardness were determined and compared. A modified direct contact test (DCT) with Enterococcus faecalis and a Streptococcus mutans' biofilm accumulation assay was carried out to evaluate the antimicrobial effect and cytotoxicity of the assay. Statistical comparisons were performed (α=5%). Results: The results showed that the physical and mechanical properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference and some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values. TFMs with ZM killed E. faecalis only after 1 h. Biofilm development of S. mutans was not affected by the inclusion of ZM in the experimental TFMs. Conclusions: The present findings suggest that the physical, mechanical and biological properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference. However, some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values.

Development and characterization of a novel bulk-fill elastomeric temporary restorative composite.

OBJECTIVES: This study investigated the physical and mechanical properties, antibacterial effect and biocompatibility of novel elastomeric temporary resin-based filling materials (TFMs) containing zinc methacrylate (ZM). MATERIAL AND METHODS: Experimental TFMs were prepared by mixing the zinc methacrylate with monomer, co-monomer, photoinitiator and fillers. A ZM concentration of 0 (control), 0.5% (Z0.5); 1% (Z1), 2% (Z2), or 5% (ZM5) wt% was added to the TFMs. Fermit-N (F) was used for comparison with the experimental material. Microleakage, water sorption/solubility, degree of conversion, depth of cure, ultimate tensile strength, and hardness were determined and compared. A modified direct contact test (DCT) with Enterococcus faecalis and a Streptococcus mutans' biofilm accumulation assay was carried out to evaluate the antimicrobial effect and cytotoxicity of the assay. Statistical comparisons were performed (α=5%). RESULTS: The results showed that the physical and mechanical properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference and some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values. TFMs with ZM killed E. faecalis only after 1 h. Biofilm development of S. mutans was not affected by the inclusion of ZM in the experimental TFMs. CONCLUSIONS: The present findings suggest that the physical, mechanical and biological properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference. However, some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values.

Piperonyl methacrylate: Copolymerizable coinitiator for adhesive compositions.

OBJECTIVES: This study describes the synthesis of piperonyl methacrylate (PipM) and evaluates its effect when used as coinitiator in the photoinitiated radical polymerization of experimental adhesive resins. METHODS: PipM was synthetized through an esterification reaction and characterized by FTIR and 1H NMR spectroscopy. Adhesive resins containing camphorquinone as photoinitiator and PipM or ethyl-4-dimethyl amine benzoate (EDAB) as coinitiators were formulated. Scotchbond Multipurpose (SBMP) adhesive was used as commercial reference. All materials were analyzed for polymerization kinetics, flexural strength, elastic modulus, water sorption/solubility, shear bond strength to bovine enamel and dentin, characterization of hybrid layer by scanning electron microscopy (SEM), microbiological direct contact test, and cytotoxicity. RESULTS: The adhesive with PipM presented higher degree of conversion and lower sorption/solubility when compared with other groups. Shear bond strength to enamel and dentin were similar for PipM and EDAB materials. The percentage of cellular viability was close to 100% and similar in the experimental groups and the commercial reference. CONCLUSIONS: PipM presented similar or superior performance to the tertiary amine used as control, representing a potential alternative coinitiator for photopolymerizable dental materials. CLINICAL SIGNIFICANCE: PipM could be potentially useful in the formulations of adhesive systems with enhanced chemical properties, which could mean improvement in the longevity of composite resin restorations.

Bond Strength of Experimental Root Canal Sealers Based on MTA and Butyl Ethylene Glycol Disalicylate.

This study investigated the bond strength of two experimental root canal sealers based on MTA and butyl ethylene glycol disalicylate: MTAe and MTAe-HA. The reference materials used for comparison were AH Plus and MTA Fillapex. Twenty human upper incisors were selected and one 1 mm slice was obtained from the cervical third of each root. On the coronal surface of each slice, four 0.9 mm wide holes were drilled through the dentine. Standardized irrigation was performed and holes were filled with one of the four tested sealers: AH Plus, MTA Fillapex, MTAe, and MTAe-HA. The filled slices were stored in a PBS solution (pH 7.2) for 7 days at 37 °C. A push-out assessment was performed with a 0.7 mm plunger tip. Load was applied at a crosshead speed of 0.5 mm/min until sealer displacement. The results were expressed in MPa. The Kruskal-Wallis test was applied to assess the effect of each sealer on the push-out bond strength. Mann-Whitney with Bonferroni correction was used to isolate the differences. The alpha-type error was set at 0.05. Significant differences among medians values obtained by materials were observed (p<0.001). AH Plus displayed the highest value of bond strength (p<0.001). In contrast, MTA Fillapex presented the lowest bond strength among all tested sealers (p<0.001). Experimental sealers showed intermediary bond strength values, with no statistical differences between them (p>0.05). In conclusion, experimental root canal sealers presented suitable bond strength outcomes when compared to MTA Fillapex.

Pentaerythritol Tetrasalicylate in the Chemical Composition of Root Canal Sealers

Abstract The aim of this study was to synthesize and evaluate physicochemical properties of a new salicylate derivative in experimental calcium-based root canal sealers. Two salicylate derivatives were synthesized for the transesterification reaction of methyl salicylate with two different alcohols (1,3-butylenoglicol disalicylate-BD and pentaerythritol tetrasalicylate -PT) in molar ratio 1:3 and 1:6, respectively. The products (BD and PT), were characterized by Fourier Transform Infrared Spectroscopy (FTIR) and Nuclear Magnetic Resonance spectroscopy (RMN). Calcium-based experimental sealers were prepared with the same catalyst paste (60% of MTA, 39% of n-ethyl-o-toluenesulfonamide, and 1% titanium dioxide) and four different concentrations of BD and PT in the base pastes (40/0 - control, 35/5, 30/10 and 20/20) with 60% of bismuth oxide. The experimental sealers were evaluated for setting time, solubility (24 h, 7, 14 and 30 days), diametral tensile strength and Young's Modulus. Data were analyzed by one- or two-way ANOVA with Tukey's test (p<0.05). The addition of PT reduced the materials setting time. After 24 h the sealer 40/0 and 35/5 had higher solubility, and after 14 and 28 days the sealer 20/20 showed the lowest solubility (p<0.05). After 7 days the sealer 20/20 stabilized its solubility. The sealer 40/0 presented the highest values and the 20/20 presented the lowest values of diametral tensile strength and Young's modulus (p<0.05). The addition of PT to calcium-based root canal sealers provides benefits to the setting time and solubility.

Resumo O objetivo neste estudo foi sintetizar e avaliar as propriedades físico-químicas de um novo derivado do salicilato em cimentos endodônticos experimentais à base de cálcio. Dois derivados de salicilato foram sintetizados por meio de uma reação de trans esterificação do salicilato de metila com dois diferentes alcoóis (1,3-butilenoglicol dissalicilato-BD e pentaeritritol tetrassalicilato-PT) na proporção molar de 1: 3 e 1:6, respectivamente. Os produtos (BD e PT), foram caracterizados por espectroscopia infravermelho transformada de Fourier (FTIR) e espectroscopia de ressonância magnética nuclear (RMN). Os cimentos experimentais à base de cálcio foram preparados com a mesma pasta catalisadora (60% de MTA, 39% de N-etil o/p toluenosulfonamida e 1% de dióxido de titânio) e quatro concentrações diferentes de BD e PT nas pastas base (40/0 - controle, 35/5, 30/10 e 20/20) com 60% de óxido de bismuto. Os cimentos foram avaliados quanto ao tempo de endurecimento, à solubilidade (24 h, 7, 14 e 28 dias), resistência à tração diametral e ao módulo de elasticidade. Os dados foram analisados por ANOVA um ou dois fatores e as médias comparadas pelo teste de Tukey (p<0,05). A adição de PT reduziu o tempo de endurecimento dos materiais testados. Após 24 horas os cimentos 40/0 e 35/5 apresentaram maior solubilidade que os demais e após 14 e 28 dias o cimento 20/20 foi o que apresentou menor solubilidade (p<0,05). Após 7 dias o grupo 20/20 estabilizou a sua solubilidade. O cimento 40/0 apresentou os maiores valores e o cimento 20/20 apresentou os menores valores de resistência à tração diametral e módulo de elasticidade (p<0,05). A adição de PT a cimentos à base de cálcio possibilita benefícios ao tempo de presa e solubilidade.

Pentaerythritol Tetrasalicylate in the Chemical Composition of Root Canal Sealers.

The aim of this study was to synthesize and evaluate physicochemical properties of a new salicylate derivative in experimental calcium-based root canal sealers. Two salicylate derivatives were synthesized for the transesterification reaction of methyl salicylate with two different alcohols (1,3-butylenoglicol disalicylate-BD and pentaerythritol tetrasalicylate -PT) in molar ratio 1:3 and 1:6, respectively. The products (BD and PT), were characterized by Fourier Transform Infrared Spectroscopy (FTIR) and Nuclear Magnetic Resonance spectroscopy (RMN). Calcium-based experimental sealers were prepared with the same catalyst paste (60% of MTA, 39% of n-ethyl-o-toluenesulfonamide, and 1% titanium dioxide) and four different concentrations of BD and PT in the base pastes (40/0 - control, 35/5, 30/10 and 20/20) with 60% of bismuth oxide. The experimental sealers were evaluated for setting time, solubility (24 h, 7, 14 and 30 days), diametral tensile strength and Young's Modulus. Data were analyzed by one- or two-way ANOVA with Tukey's test (p<0.05). The addition of PT reduced the materials setting time. After 24 h the sealer 40/0 and 35/5 had higher solubility, and after 14 and 28 days the sealer 20/20 showed the lowest solubility (p<0.05). After 7 days the sealer 20/20 stabilized its solubility. The sealer 40/0 presented the highest values and the 20/20 presented the lowest values of diametral tensile strength and Young's modulus (p<0.05). The addition of PT to calcium-based root canal sealers provides benefits to the setting time and solubility.

Influence of addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride to an experimental adhesive.

The aim of this study was to develop an experimental adhesive with addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride (METAC) and to evaluate its mechanical and biological properties and its in vitro antibacterial activity. An experimental adhesive resin was formulated with Bis-GMA, TEGDMA, and HEMA. The antibacterial monomer was added at concentrations of 1%, 2.5%, and 5% (METAC groups). A group without METAC addition was used as control. The experimental adhesives were evaluated as to their antibacterial potential against Streptococcus mutans, degree of conversion, and softening in ethanol for 2 hours. The data were analyzed by one-way ANOVA, Tukey's post-hoc test, and the paired Student's t-test (significance level of 0.05). METAC showed antibacterial activity against S. mutans at all concentrations (p < 0.05). There was no statistical difference across METAC groups (p > 0.05). The 1%, 2.5%, and 5% groups yielded the highest mean values for degree of conversion (p < 0.05). The 1% group did not differ from the control group (p > 0.05). There was no statistical difference in baseline microhardness values (p > 0.05) and microhardness values after immersion in ethanol were lower than at baseline for all groups (p < 0.05). There was no statistical difference in the reduction of Knoop hardness number (KHN) after immersion in ethanol for any of the groups (p > 0.05). The results of the present study indicate that METAC is a promising antibacterial agent when added to an adhesive system.

Triazine Compound as Copolymerized Antibacterial Agent in Adhesive Resins.

The aim of this study was to formulate and evaluate an experimental adhesive resin with the addition of 1,3,5-triacryloylhexahydro-1,3,5-triazine at different concentrations. Experimental adhesive resins were obtained by mixing 50% wt bisphenol A glycol dimethacrylate (BisGMA), 25% wt triethylene glycol dimethacrylate (TEGDMA), 25% wt 2-hydroxyethyl methacrylate (HEMA) and photoinitiator system. The triazine compound was added in 1, 2.5 and 5% wt to a base adhesive resin and one group remained with no triazine as control group. The experimental adhesive resins were analyzed for antibacterial activity (n=3), degree of conversion (n=3) and softening in solvent (n=3). Data distribution was evaluated by Kolmogorov-Smirnov test, paired t test, one-way ANOVA and Tukey's with a 0.05 level of significance. All groups with added triazine compound showed antibacterial activity against Streptococcus mutans (p<0.05). All groups achieved more than 70% degree of conversion, but there was no difference in this chemical property (p>0.05). The initial Knoop hardness was higher in 2.5 and 5% wt groups (p<0.05) and both groups present lower percentage variation of Knoop hardness after solvent degradation. The present study formulated an antibacterial adhesive resin with a non-releasing agent able to copolymerize with the comonomeric blend, improving the restorative material's properties.

Addition of ammonium-based methacrylates to an experimental dental adhesive for bonding metal brackets: Carious lesion development and bond strength after cariogenic challenge.

INTRODUCTION: In this study, we evaluated the caries inhibition and shear bond strength achieved with the addition of the antibacterial monomer [2-(Methacryloyloxy)ethyl] trimethylammonium chloride (MADQUAT) to an adhesive used to bond orthodontic brackets. METHODS: Experimental adhesives were formulated with addition of 0% (control), 5%, or 10% MADQUAT followed by measurement of the degree of conversion. These adhesives were used to lute brackets to the enamel of premolars (n = 30). Biofilm from a microcosm model was cultivated in half of the specimens under cariogenic challenge for 5 days. The brackets were subjected to a shear bond strength test followed by measurement of the internal hardness of the enamel around the brackets to calculate the integrated mineral loss. RESULTS: The addition of MADQUAT slightly increased the degree of conversion. Adhesive containing 10% MADQUAT significantly reduced the integrated mineral loss around the bracket but also resulted in the lowest values of bond strength. No effects on bond strength and integrated mineral loss were observed with the addition of 5% MADQUAT to the adhesive. The cariogenic challenge did not affect the bond strength and the failure mode. CONCLUSIONS: MADQUAT was effective to reduce the integrated mineral loss only when added to the adhesive at a concentration of 10% despite the reduction of bond strength.

Triazine Compound as Copolymerized Antibacterial Agent in Adhesive Resins

Abstract The aim of this study was to formulate and evaluate an experimental adhesive resin with the addition of 1,3,5-triacryloylhexahydro-1,3,5-triazine at different concentrations. Experimental adhesive resins were obtained by mixing 50% wt bisphenol A glycol dimethacrylate (BisGMA), 25% wt triethylene glycol dimethacrylate (TEGDMA), 25% wt 2-hydroxyethyl methacrylate (HEMA) and photoinitiator system. The triazine compound was added in 1, 2.5 and 5% wt to a base adhesive resin and one group remained with no triazine as control group. The experimental adhesive resins were analyzed for antibacterial activity (n=3), degree of conversion (n=3) and softening in solvent (n=3). Data distribution was evaluated by Kolmogorov-Smirnov test, paired t test, one-way ANOVA and Tukey’s with a 0.05 level of significance. All groups with added triazine compound showed antibacterial activity against Streptococcus mutans (p<0.05). All groups achieved more than 70% degree of conversion, but there was no difference in this chemical property (p>0.05). The initial Knoop hardness was higher in 2.5 and 5% wt groups (p<0.05) and both groups present lower percentage variation of Knoop hardness after solvent degradation. The present study formulated an antibacterial adhesive resin with a non-releasing agent able to copolymerize with the comonomeric blend, improving the restorative material’s properties.

Resumo O objetivo desse estudo foi desenvolver e avaliar a adição de 1,3,5-triacryloylhexahydro-1,3,5-triazine a uma resina adesiva experimental em diferentes concentrações. Resinas adesivas experimentais foram obtidas a partir da mistura de 50% em peso de bisphenol A glycol dimethacrylate (BisGMA), 25% em peso de triethylene glycol dimethacrylate (TEGDMA), 25% em peso de hidroxietil metacrilato (HEMA) e sistema fotoiniciador. O composto de triazina foi adicionado em proporções de 1; 2,5 e 5% em peso a resina adesiva base e um grupo permaneceu sem a adição do composto de triazina como grupo controle. As resinas adesivas experimentais foram analisadas por atividade antibacteriana (n=3), grau de conversão (n=3) e degradação em solvente (n=3). A distribuição dos dados foi avaliada por teste de Kolmogorov-Smirnov, teste t pareado, ANOVA de uma via e Tukey, considerando nível de significância de 5%. Todos os grupos com adição de composto de triazina demonstraram atividade antibacteriana contra Streptococcus mutans (p<0,05). Todos os grupos atingiram mais de 70% de grau de conversão, mas não houve diferença estatística para essa propriedade química (p>0,05). A dureza Knoop inicial foi maior para os grupos com 2,5 e 5% de triazina (p<0,05) e ambos os grupos apresentaram menor variação percentual de dureza Knoop após degradação em solvente. No presente estudo, foi produzida uma resina adesiva antibacteriana com agente sem liberação para o meio, capaz de copolimerizar com a blenda comonomérica, melhorando as propriedades do material restaurador.

Influence of an iodonium salt on the properties of dual-polymerizing self-adhesive resin cements.

STATEMENT OF PROBLEM: Dual-polymerizing self-adhesive resin cements present mechanical properties that may adversely affect the clinical performance of luted fiber-reinforced posts. PURPOSE: The purpose of this in vitro study was to evaluate the properties of dual-polymerizing self-adhesive resin cements after the addition of an onium salt. MATERIAL AND METHODS: The experimental groups were set according to the molar concentration of diphenyliodonium hexafluorphosphate (DPIHFP) (0.5, 1, and 2 mol%). The resin cements were submitted to a push-out bond strength test and assessed for flexural strength (ISO 4049/2009), degree of conversion (Fourier-transformed infrared spectroscopy), depth of polymerization, swelling coefficient, and degradation in solvent. The data were statistically analyzed by ANOVA, Tukey test, Kruskal-Wallis test, Dunn multiple comparison, and paired Student t test (α=.05). RESULTS: All the RelyX U100 groups with onium salt showed the highest degree of conversion after 24 hours and 7 days (P<.001). However, no statistical difference was found among the BisCem groups (P=.054). The addition of 0.5 mol% DPIHFP increased the push-out bond strength and microhardness of RelyX U100 and promoted less degradation after immersion in solvent. The BisCem control group did not present a statistical difference from the experimental groups in terms of bond strength; the control group and the 0.5 mol% group showed no degradation in solvent. For swelling coefficient and flexural strength, no difference was found between the BisCem groups (P=.067 and P=.173), and the RelyX U100 2 mol% group presented the lower value (P<.001 and P=.048). Depth of polymerization was not statistically different in the experimental groups for either resin cement (P=.999). CONCLUSIONS: The addition of 0.5 mol% DPIHFP improved the physical properties of dual-polymerizing self-adhesive resin cements.

Influence of addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride to an experimental adhesive

Abstract The aim of this study was to develop an experimental adhesive with addition of [2-(methacryloyloxy)ethyl]trimethylammonium chloride (METAC) and to evaluate its mechanical and biological properties and its in vitro antibacterial activity. An experimental adhesive resin was formulated with Bis-GMA, TEGDMA, and HEMA. The antibacterial monomer was added at concentrations of 1%, 2.5%, and 5% (METAC groups). A group without METAC addition was used as control. The experimental adhesives were evaluated as to their antibacterial potential against Streptococcus mutans, degree of conversion, and softening in ethanol for 2 hours. The data were analyzed by one-way ANOVA, Tukey’s post-hoc test, and the paired Student’s t-test (significance level of 0.05). METAC showed antibacterial activity against S. mutans at all concentrations (p < 0.05). There was no statistical difference across METAC groups (p > 0.05). The 1%, 2.5%, and 5% groups yielded the highest mean values for degree of conversion (p < 0.05). The 1% group did not differ from the control group (p > 0.05). There was no statistical difference in baseline microhardness values (p > 0.05) and microhardness values after immersion in ethanol were lower than at baseline for all groups (p < 0.05). There was no statistical difference in the reduction of Knoop hardness number (KHN) after immersion in ethanol for any of the groups (p > 0.05). The results of the present study indicate that METAC is a promising antibacterial agent when added to an adhesive system.

Influence of different fillers on the properties of an experimental vinyl polysiloxane.

The aim of the study was to evaluate the effect of the incorporation of different fillers on an experimental vinyl polysiloxane (VPS) at two different concentrations, 20% and 40%. Different fillers were added to an experimental VPS. The study was developed in two stages: (i) incorporation of fillers in different concentrations: (a) 20 wt% fillers, and (b) 40 wt%. The fillers were added to experimental VPS and mixed with a speed mixer; (ii) characterization of experimental VPS; after the base paste and catalyst paste were mixed, the experimental VPS was used to make specimens specifically for each test, which were stored at 23°C for 24 hours. The tests were designed according to the specific standardization for the analysis of tensile strength, detail reproduction, Shore A hardness, and elastic recovery. For analysis of filler size pattern, scanning electron microscopy at 1500× magnification was used. The aerosil OX-50 40% (AE), and pure aluminum hydroxide 40% (PAH) groups presented the highest tensile strength and Shore A hardness values. However, those were the only groups that did not present continuous detail reproduction of an intersection of 20 µm line. The elastic recovery was not statistically significant. The undesirable characteristics of VPS (lowest Shore A hardness and tensile strength) were observed when it was added to the composition of acrylic polymer (AP) and fiberglass (FG) in both concentrations, 20% and 40%. In groups AE and PAH, agglomerates of nanofillers were shown in SEM micrography, while the other groups presented different shapes and fillers sizes.